TIG WELDING Rods and Flux for TIG welding Welding rods Product
4.02
Product no.
Description
IMS-210 097-604850
2.0 mm
Unitor IMS is a welding rod for unalloyed and low alloyed steels. Rods with diameter 2.0mm are most used for TIG welding.
ICROMO-216 097-305532
2.5 mm
lcromo is a chromium-molybdenum alloyed welding rod for heat resistant steels types 10 Cr Mo-910 and 13 Mo-44 found in boiler tubes and other heat resistant components. Tensile strength
560 Mpa.
18/8 Mo-221 097-602979
2.0 mm
18/8 Mo is a wire for welding stainless and acid resistant steel. The silisium content of the wire ensures smooth transfer and good profile of the bead. Application areas are similar to the coated electrode 18/8-321 N in 1.7 mm, but with the advantages TIG can offer. When welding very thin sheets and pipes (less than 2mm) it is always an advantage to use the TIG process. This is also an advantage for the root bead when welding thicker sheets with prepared V-grooves.
IDUPLEX-222 097-725309
2.0 mm
Iduplex-222 is at TIG rod for welding Duplex stainless steel, Duplex to Mild steel and Duplex to Stainless steel. The deposit offers elevated mechanical strength and toughness reistance to stress corrosion cracking. It is an advantage to use TIG welding in thin sheets and pipe walls. Can also be used for welding the root run in thick wall piping where the rest of the groove is filled up using the duplex electrode Duplex-325 N.
ALUMAG-235 092-514265
3,0 mm
A welding rod for Gas and TIG welding of wrought and cast alumimum alloys containing up to 5 % Mg.
ICUNI-30-239 097-335547
2.5 mm
A welding rod for TIG welding of copper nickel alloys, for example Cunifer pipes. No flux is used in this process. Typical applications are welding flanges on pipes, pipe joints, patching leaking pipes etc. Joint surfaces and adjacent areas must be thoroughly cleaned before welding. Small diameter Cunifer pipes can be joined by means of overlap joints (capillary action) using AG-60 silver solder combined with AG-60 Flux.
IALBRO-237 MF 097-519736
2.4 mm
IALBRO is a flux-coated filler rod for TIG welding of aluminiumbrass pipes (Yorcalbro). This type of alloy is widely used in seawater resistant piping. In TIG welding of joints it is strongly recommended that I-Flux 238 be applied to both sides of the joint on the inside. Yorcalbro pipes with a diameter less than 4” which can be joined by means of an overlap joint (capillary action) may be silver brazed using AG-60 combined with Albro Flux.
IFLUX-238 PF
097-603092
Unitor flux is supplied in paste form for use with the TIG rod Ialbro-237 MF for welding of Yorcalbro. The flux is complementary to the flux found in the serrations of the lalbro TIG rod. While the flux on the rod is sufficient for the actual welding zone, it is strongly recommended to use additional IFLUX on both sides of the joint, especially on the inside of e.g. pipes. This will improve bonding and penetration. Flux residues must be washed off with water after welding. IFLUX is supplied in 250 gram tins.
Tech sheets for all above products under section Consumables.